Título: Análise da influência da cal hidratada na aderência das argamassas de revestimento em obras das Regiões Centro-Oeste e Sul a partir do ano de 2010
Título(s) alternativo(s): Analysis of the influence of hydrated lime on the adhesion of coating mortars in works from Central-West and Southern Regions from 2010
Autor(es): Xavier, Fellipe Alves
Primeiro Orientador: Silva Júnior, Paulo Francinete
metadata.dc.contributor.advisor-co1: Coelho, Sérgio Azevedo
metadata.dc.contributor.referee1: Silva Júnior, Paulo Francinete
metadata.dc.contributor.referee2: Ferreira, Ricardo de Alcântara
metadata.dc.contributor.referee3: Alves, Cláudio Marra
Resumo: A aderência é uma propriedade, referente interface entre substratos e revestimentos argamassados, que, mesmo nos dias atuais, gera inúmeras ocorrências de manifestações patológicas do tipo fissuras ou desplacamento de revestimentos. Ainda, essas manifestações patológicas, bastante frequente em obras de pequeno e médio porte, são comumente relacionadas a, entre outros fatores, o excesso de cal no traço de argamassa. Tal problemática é atribuída a falta de um traço padrão e controle tecnológico na produção de argamassas de revestimento de obras de pequeno e médio porte. Dessa forma, o presente trabalho tem como proposta estudar a influência gerada pela cal, presente em traços de argamassa de revestimento, na resistência a aderência da interface substrato/revestimento argamassado a partir do ensaio de resistência a tração na flexão (ensaio de arrancamento). Para isso, leva-se em consideração ensaios realizados nas regiões Centro-Oeste e Sul, a partir do ano de 2010, por pesquisadores terceiros, em três trabalhos base. Os trabalhos que serviram de base para o desenvolvimento do seguinte trabalho, foram desenvolvidos com dois ou mais traços diferentes entre proporções e tipos de materiais, principalmente o tipo da cal hidratada. Em seguida, foram apresentados os ensaios desenvolvidos por cada autor em seu respectivo trabalho e a apresentação e análise dos resultados obtidos em cada ensaio desenvolvido. Por fim, concluiu-se que a cal pode ser um fator tanto benéfico, quanto prejudicial, para a resistência de aderência à tração das argamassas de revestimento. A proporção de cal nos traços deve ser estudada e bem definida, pois com pouca ou muita quantidade de cal o revestimento vai perdendo sua capacidade de aderência. Sendo assim, dos traços analisados nos três trabalhos, o que obteve melhor desempenho foi 1:1:6 de cimento CP-II-Z, cal hidratada CH-III e areia natural média, com uma resistência de 0,89 Mpa.
Abstract: Adhesion is a property reggarding to the interface between substractes and mortar coatings, that even nowadays, causes many pathologies occurences such as cracks and detachment of coats. These patholgies, quite common in small and medium-sized work, are usually related, among others factors, to excess of lime in the mortar mix. Such problem is attributed to the lack of a standard feature and technological control in the production of coating mortars for small and medium-sized works. Thus, the present work proposes to study the influence generated by lime, present in traces of coating mortar, on the adhesion resistance of the substrate/mortar coating interface from the flexural tensile strength test (pullout test). For that, it takes into consideration tests carried out in the Midwest and South regions, from the year 2010, by third researchers, in three basic studies. The works that served as a basis for the development of the following work, were developed with two or more different features between proportions and types of materials, mainly the type of hydrated lime. Then, the developed essays, by each author, were presented such as the analysis of the results obtained. Finally, it was concluded that lime can be both a beneficial and a detrimental factor for the tensile strength of the coating mortars. The proportion of lime in the lines must be studied because with little or a lot of lime the coating might lose its ability to adhere. Therefore, of the lines analyzed in the three studies, the one that obtained the best performance was 1: 1: 6 of CP-II-Z cement, hydrated lime CH-III and medium natural sand, with a resistance of 0.89 Mpa.
Palavras-chave: Aderência
Argamassa
Cal
Revestimento
CNPq: CNPQ::ENGENHARIAS::ENGENHARIA CIVIL::CONSTRUCAO CIVIL::MATERIAIS E COMPONENTES DE CONSTRUCAO
Idioma: por
País: Brasil
Editor: Insitituto Federal de Educação, Ciência e Tecnologia de Goiás
Sigla da Instituição: IFG
metadata.dc.publisher.department: Câmpus Goiânia
Citação: XAVIER, Fellipe Alves. Análise da influência da cal hidratada na aderência das argamassas de revestimento em obras das regiões centro-oeste e sul a partir do ano de 2010. 2020. 130f. Trabalho de conclusão de curso (Bacharelado em Engenharia Civil), Instituto Federal de Goiás, Goiânia, 2020.
Tipo de Acesso: Acesso Aberto
URI: http://repositorio.ifg.edu.br:8080/handle/prefix/803
Data do documento: 22-Mar-2021
Aparece nas coleções:Bacharelado em Engenharia Civil

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
tcc_ Felipe Alves Xavier.pdf2,48 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.